Teflon® PFA D 335D

Category:	PFA , Perfluoroalkoxy
Manufacturer:	DuPont Fluoropolymers
Trademark:	Teflon® PFA
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MQw4pl_Teflon-PFA-D-335D.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DuPont™ Teflon ® PFAD 335D is an off-white aqueous perfluoroalkoxy (PFA) dispersion stabilized with a non-ionic surfactant. It is a general-purpose dispersion that can be used to impart some the unique properties of PFA to end products that would be difficult to make using traditional melt extrusion processes. It can be used to coat or impregnate porous structures or to make thin films. It can be coated and melt bonded to polytetrafluoroethylene (PTFE) resin or used as a hot melt adhesive.

The PFA resin in PFAD 335D is a melt flowable thermoplastic, providing superior properties typical of fluoropolymer resins: retention of properties after service at 260 °C (500 °F) and useful properties at -240 °C (-400 °F).

PFAD 335D aqueous dispersion provides:

inertness to nearly all industrial chemicals and solvents

stability at high temperatures

excellent dielectric properties

excellent weatherability

excellent anti-stick properties

Typical Applications

Heat-sealable top coatings for PTFE-coated fabrics for belting, circuit boards, architectural fabrics and electrical insulation

Cast film for capacitor dielectrics or chemical barriers

Holt melt adhesive for PTFE, PFA and FEP parts

Metal coatings

General Information
Features	Food Contact Acceptable Good Chemical Resistance Good Electrical Properties Good Weather Resistance Non-Stick Solvent Resistant
Uses	Adhesives Cast Film Coating Applications Film
Agency Ratings	EU 10/2011 FDA 21 CFR 177.1550
Forms	Dispersion
Processing Method	Cast Film Coating Dip Coating Spraying

Physical	Nominal Value	Unit	Test Method
Density ¹	1.50	g/cm³	ISO 12086, ASTM D4441
Melt Mass-Flow Rate (MFR) (372°C/5.0 kg)	2.0	g/10 min	ASTM D2116, ISO 12086
Average Particle Size	200	nm	Internal Method
pH
--	10.0		ASTM E70
--	10.0		ISO 1148
Solids Content - % PFA by weight
--	60	%	ASTM D4441
--	60	%	ISO 12086

Fill Analysis	Nominal Value	Unit	Test Method
Brookfield Viscosity
25°C	25	mPa·s	ISO 2555
25°C	25	mPa·s	ASTM D2196

Additional Information	Nominal Value	Unit	Test Method
Surfactant Content - based on PFA solids
--	6.0	%	ISO 12086
--	6.0	%	ASTM D4441

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	305	°C	ISO 12086, ASTM D2116

Note Message
1 .	at 60% solids

Resin Grade	Manufacturer	Category	Trademark
Anjacom® 250-GFK20/10	Almaak International GmbH	Nylon 6	Anjacom®
DOMAMID® 66G30V0EF	DOMO Engineering Plastics SPA	Nylon 66	DOMAMID®
Durethan® DP A 30 S FN30 DUS025 000000	LANXESS Asia/Pacific	Nylon 66	Durethan®
TECHNYL STAR® S 60G1 V30 GREY R7035 CF	Solvay Engineering Plastics	Nylon 6	TECHNYL STAR®
Enable™ 27-05HH	ExxonMobil Chemical	mPE	Enable™