PLURIS 4303
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | PLURIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MPvBgI_PLURIS4303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pluris4303 is a Braskem Quaterpolymer produced with Spherilene technology. This grade show unique properties, such as high stiffness associated with toughness. In addition to good processability, also shows a very good bubble stability and very low gel content. Applications: Thin films and automatic packaging which require higher stiffness: textile products, toilet paper and others. Additive: Antiblocking medium Slip medium Process: Blown Film Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 40 µm, blown film | 30.0 | MPa | ASTM D882 |
| TD : Broken, 40 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 40 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 40 µm, blown film | 1300 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 40 µm, Blown Film | 240 | MPa | ASTM D790 |
| 1% Secant, TD : 40 µm, Blown Film | 300 | MPa | ASTM D790 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, blown film | 30 | g | ASTM D1922 |
| TD : 40 µm, blown film | 1100 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 40.0 µm, Blown Film) | 57 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 55T1030 | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PPcompound |
| TEKAMID™ TA210G15 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Badaflex® TPE-S 70A 1000LD | Bada AG | TPE | Badaflex® |
| Centrex® 485CS | Network Polymers, Inc. | ASA | Centrex® |
| Latan 13 E71 | LATI S.p.A. | Acetal (POM) Copolymer | Latan |