EPO-TEK® T7109-18
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MPt3Us_EPO-TEK-T7109-18.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A flexible, electrically insulating epoxy paste designed for low stress and heat dissipation applications. Alternative to EPO-TEK® T7109-17. Formerly 52-183M |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 294 | °C | |
| Die Shear Strength - >1 kg (23°C) | 2.34 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 125 | °C | |
| Intermittent | -55 to 225 | °C | |
| Storage Modulus (23°C) | 9.87 | MPa | |
| Thixotropic Index | 2.20 | ||
| Weight Loss on Heating | |||
| 200°C | 0.50 | % | |
| 250°C | 1.2 | % | |
| 300°C | 4.5 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | < 5.00 | °C | |
| CLTE - Flow | |||
| -- 2 | 6.8E-5 | cm/cm/°C | |
| -- 3 | 2.0E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 2.0 | ||
| Shelf Life (23°C) | 26 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Clear/Transparent | ||
| -- 5 | Grey | ||
| Density | |||
| Part B | 1.07 | g/cm³ | |
| Part A | 1.86 | g/cm³ | |
| Viscosity 6(23°C) | 6.5 to 11 | Pa·s | |
| Curing Time (80°C) | > 2.0 | hr | |
| Pot Life | 90 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 69 | ||
| Lap Shear Strength (23°C) | 1.50 | MPa | |
| Relative Permittivity (1 kHz) | 5.63 | ||
| Volume Resistivity (23°C) | > 5.0E+9 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.070 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594B-G70E-M | TSRC Corporation | SEBS | T-Blend® |
| WanBlend® WHT-HF8675 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| ZYLAR® 960 | INEOS Styrolution Group GmbH | MMBS | ZYLAR® |
| LNP™ LUBRICOMP™ DFL36G compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Jam 526F2BX | Jam Petrochemical Company | HDPE | Jam |