Celstran® PP-GF30-02 AD 3002
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MOrYcP_Celstran-PP-GF30-02-AD-3002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% long strand glass fiber reinforced polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 8690 | MPa | ASTM D638 |
| 23°C | 6410 | MPa | ASTM D638 |
| 93°C | 3790 | MPa | ASTM D638 |
| -- | 5800 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 141 | MPa | ASTM D638 |
| Fracture, 23°C | 108 | MPa | ASTM D638 |
| Fracture, 93°C | 66.9 | MPa | ASTM D638 |
| Fracture | 92.0 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 2.1 | % | ASTM D638 |
| Fracture, 23°C | 2.4 | % | ASTM D638 |
| Fracture, 93°C | 2.8 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 200 - 210 | °C | |
| Middle Temperature | 210 - 220 | °C | |
| Front Temperature | 220 - 230 | °C | |
| Nozzle Temperature | 230 - 240 | °C | |
| Processing (Melt) Temp | 230 - 240 | °C | |
| Mold Temperature | 40.0 - 70.0 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 230 to 240°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® WC (92 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Borealis PE VS4470 | Borealis AG | HDPE | Borealis PE |
| Arak HDPE EX3B (GM5010T2) | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Karina WHITE PVC COMPOUND 651D10/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8260-65FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |