SAXALEN™ PPH329B20
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXALEN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MOmp4r_SAXALEN-PPH329B20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXALEN PPH329B20 is a 20% glass beads filled Polypropylene - Homopolymer intended for injection moulding. Low shrinkage, low warpage grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Flexural Stress 2 | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.0 | kJ/m² | |
| 23°C | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 27 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris POM HI511 | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| Formolene® L42022E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| LUVOCOM® 1800-8449 | Lehmann & Voss & Co. | PET | LUVOCOM® |
| Teldene® H06ML | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| SABIC® LLDPE 218BE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |