LNP™ THERMOCOMP™ HF008 compound
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MOWQ0Q_LNPTHERMOCOMPHF008compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP HF008 is a compound based on Nylon 11 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound HF-1008 Product reorder name: HF008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 - 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.80 - 1.0 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9280 | MPa | ASTM D638 |
| -- | 7600 | MPa | ISO 527-2/1 |
| Tensile Strength (Break) | 123 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 4.9 | % | ASTM D638 |
| Fracture | 3.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8480 | MPa | ASTM D790 |
| -- | 7970 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 221 | MPa | ASTM D790 |
| -- | 192 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 240 | J/m | ASTM D256 |
| 23°C 2 | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 76 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.7 | J | ASTM D3763 |
| -- | 3.51 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 178 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 175 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 2.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.9E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP400M | LyondellBasell Industries | PP, Unspecified | Moplen |
| 4TECH® 9S22110 | 4Plas | Polyphenylene, Unspecified | 4TECH® |
| LEXAN™ ML7647K resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ STAT-KON™ DX04489C compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Sylvin 8948-70 Red 654 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |