Latiohm 88/10-06 CNT
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiohm |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MONZoR_Latiohm-88-10-06-CNT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Partially conductive/dissipative compound based on Polyetheretherketone (PEEK). Carbon nanotubes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.2 to 1.6 | % | |
| Flow : 2.00 mm | 1.2 to 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 175 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 50 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 295 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 300 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 2.0E+4 | ohms·cm | ASTM D257 |
| Electromagnetic Reflection 2 | 88 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 360 to 390 | °C | |
| Mold Temperature | 170 to 200 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | Bekiscan - CP |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP M1500 | LG Chem Ltd. | PP Impact Copolymer | SEETEC PP |
| Calprene® H6140 | Dynasol Elastomers | SEBS | Calprene® |
| Hipolyene 7151 M1 HF | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Hostacom EBG733T | LyondellBasell Industries | PP Copolymer | Hostacom |
| Panlite® MN-3705 | TEIJIN LIMITED | PC | Panlite® |