ISOPAK® 547HF
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Great Eastern Resins Industrial Co Ltd (GRECO) |
| Trademark: | ISOPAK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MODBnA_ISOPAK-547HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ISOPAK® 547HF is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific, Europe, or North America. Important attributes of ISOPAK® 547HF are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, 3.18 mm) | 43.1 | MPa | ASTM D638 |
| Flexural Strength 1(Yield, 23°C) | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) 2(23°C) | 19.6 | kJ/m² | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.8 mm/min |
| 2 . | 1/4" x 1/2" x 5/2" sample |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2500 UV | RTP Company | PC+ABS | RTP |
| NuSil R3-2160 | NuSil Technology | Silicone | NuSil |
| Celstran® TPU-GF40-01 | Celanese Corporation | TPU, Unspecified | Celstran® |
| ELASTOSIL® R 750/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| API II 392 | API II, Inc. | PS (GPPS) | API II |