Vipel® F017-AA-00
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MNgPC8_Vipel-F017-AA-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vipel Elastomeric Bisphenol A, Epoxy Vinyl Ester Resin The Vipel F017 Series are elastomeric, bisphenol A epoxy vinyl ester resins. Vipel F017-AAA-00 is a non-promoted, non-thixotropic resin that can be formulated as needed. Low VOC content Versions are available that are less than 40% styrene. Bonding AOC's Vipel F017 Series resins are designed as a primer for bonding fiberglass laminates to steel and other substrates. Resilience It can also be used to manufacture hand lay-up, spray-up or filament wound parts that require a great deal of resilience. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | |
| Styrene Content | 40 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Exotherm | |||
| Gel to Peak | 6.0 | min | |
| Peak | 177 | °C | |
| Gel Time (25°C) 1 | 15.0 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 35 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3380 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 73.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 9.1 | % | ASTM D638 |
| Flexural Modulus | 3380 | MPa | ASTM D790 |
| Flexural Strength | 118 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 92.8 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 2(25°C) | 350 | cP |
| Note Message | |
|---|---|
| 1 . | Gel time with 0.5% Cobalt 6%, 0.3% DMA and 2.0% MEKP |
| 2 . | Brookfield RV viscosity spindle 2 at 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 6329 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| ResMart Ultra CoPP 4-NB | ResMart | PP Impact Copolymer | ResMart Ultra |
| SOLLAMID A 2730 FV 33 | Krisoll Resinas Plásticas Ltda. | Nylon 66 | SOLLAMID |
| TEREZ PA 10.10 7500 GF 30 ECO | TER HELL PLASTIC GMBH | Nylon 1010 | TEREZ PA 10.10 |
| LNP™ STAT-KON™ AX02747 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-KON™ |