Derakane® Momentum 510C-350
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | Ashland Performance Materials |
| Trademark: | Derakane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MMCpGy_Derakane-Momentum-510C-350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DERAKANE MOMENTUM® 510 C-350 is a brominated epoxy vinyl ester resin that offers a high degree of fire retardance while providing excellent chemical resistance and toughness. Optimum fire retardance is achieved when antimony compounds are added to the resin. Laminates made with DERAKANE MOMENTUM 510 C-350 resin have met ASTM E-84 Flame Spread "Class 2" rating (less than 75). With the use of antimony synergists, "Class 1" ratings can be achieved. APPLICATIONS AND USE DERAKANE MOMENTUM 510 C-350 resin is designed for ease of fabrication using hand lay-up, spray-up, filament winding, compression molding, resin transfer molding and pultrusion techniques. This resin is used extensively in FRP duct work, stacks and stack-liner applications. It is also suitable for equipment handling mixtures of air and hot gases, building panels and flooring compounds where a degree of ignition inhibiting properties are needed. DERAKANE MOMENTUM 510 C-350 resin resists mechanical and chemical damage enabling use in various caustic environments such as sodium hypochlorite, chlorine dioxide and alkaline hydrogen peroxide. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Solution Viscosity | 420 | mPa·s | |
| Styrene Content | 35 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Volume Shrinkage | 7.8 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 35 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 3170 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 82.7 | MPa | ASTM D638 |
| -- | 86.0 | MPa | ISO 527-2 |
| Tensile Elongation (Yield) | 5.0 - 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 3380 | MPa | ASTM D790 |
| -- | 3400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 152 | MPa | ASTM D790 |
| -- | 150 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 105 | °C | ISO 75-2/A |
| Glass Transition Temperature | |||
| -- | 121 | °C | ASTM D3418 |
| -- | 120 | °C | ISO 11357-2 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Properties of clear casting at 25°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPERBI 8.0 | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| Sinpolene MBB7512 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| POLYfill PPH TS4020 | Polykemi AB | PP Homopolymer | POLYfill |
| StarClear® 1040-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarClear® |
| LGH 3012 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGH |