| PTFE/Silicone lubricated |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2200 | MPa | ASTM D790 |
| Flexural Strength 3 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 125 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Mold Temperature | 90.0 - 110 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECDUR® GF 20 VO NS | LEIS Polytechnik - polymere Werkstoffe GmbH | PBT | TECDUR® |
| BP Flex 9000 VPL BLK | Buckeye Polymers, Inc. | TPV | BP Flex |
| Hostacom SB224-2 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ COLORCOMP™ J1000Z-WH9G618 compound | SABIC Innovative Plastics Europe | PESU | LNP™ COLORCOMP™ |
| Sylvin 3230-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |