Terralene® LL 1101
| Category: | HDPE+LLDPE , High Density Polyethylene + LLDPE |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Terralene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MLOqvG_Terralene-LL-1101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Linear low density polyethylene, butene copolymer, blended with high-density polyethylene, contains processing additives. Suitable for blown film applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 to 0.85 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 0.900 to 1.10 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 330 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 11.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 23 | % | |
| Break | > 300 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested 1 | 20 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 20 µm | 290 | MPa | |
| TD : 20 µm | 310 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm | 37.0 | MPa | |
| TD : Yield, 20 µm | 32.0 | MPa | |
| MD : Break, 20 µm | 36.0 | MPa | |
| TD : Break, 20 µm | 31.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Yield, 20 µm | 680 | % | |
| TD : Yield, 20 µm | 690 | % | |
| MD : Break, 20 µm | 680 | % | |
| TD : Break, 20 µm | 690 | % | |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 20.0 µm | 50.0 | kN/m | |
| TD : 20.0 µm | 150.0 | kN/m | |
| Spencer Impact (20.0 µm) | 130.0 | kN/m | ASTM D3420 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content - Carbon | 90 | % | ASTM D6866 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 to 145 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | BUR 2.4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Kepamid® 1330GFS | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| HOPELEN J-170H | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| LNP™ THERMOCOMP™ VF008A compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Lushan M-8D | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |
| SABIC® PPcompound 7251U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |