Sarlink® TPV 4775B42
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MIlyVF_Sarlink-TPV-4775B42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink® 4000 series are engineered materials designed for demanding automotive applications. Sarlink® X4775-42 exhibits excellent compression set and weatherability. The material is developed for injection molded applications featuring high flow and UV stability. Applications include window encapsulation, spoiler extensions and other intricate and high flow demanding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.908 | g/cm³ | ASTM D792 |
| -- | 0.910 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A, 5 seconds, extruded | 74 | ASTM D2240, ISO 868 | |
| Shore A, 5 seconds, injection molding | 76 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Transverse flow : 100% strain | 3.20 | MPa | ASTM D412, ISO 37 |
| Flow : 100% strain | 3.40 | MPa | ASTM D412, ISO 37 |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 6.30 | MPa | ASTM D412, ISO 37 |
| Flow : Fracture | 5.80 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 470 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 410 | % | ASTM D412, ISO 37 |
| Tear Strength - Across Flow | |||
| -- | 31.5 | kN/m | ASTM D624 |
| -- 1 | 31 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 24 | % | ASTM D395, ISO 815 |
| 70°C, 22 hr | 39 | % | ASTM D395, ISO 815 |
| 125°C, 70 hr | 56 | % | ASTM D395, ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -18 | % | ASTM D573, ISO 188 |
| 100% strain, 135°C, 1000 hr | 3.0 | % | ASTM D573 |
| 150°C, 168 hr | -19 | % | ASTM D573, ISO 188 |
| 100% strain, 150°C, 168 hr | 2.0 | % | ASTM D573 |
| 100% strain 135°C, 1000 hr | 3.0 | % | ISO 188 |
| 100% strain 150°C, 168 hr | 2.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -28 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | -24 | % | ASTM D573, ISO 188 |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Support a, 135°C, 1000 hr | -2.0 | ASTM D573, ISO 188 | |
| Support a, 150°C, 168 hr | 1.0 | ASTM D573, ISO 188 | |
| Change in Volume | |||
| 125°C, 70 hr, in IRM 903 oil | 73 | % | ASTM D471 |
| 125°C, 70 hr, in IRM 903 oil | 73 | % | ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary @ 206/s | |||
| 200°C | 200 | ISO 11443 | |
| 200°C | 200 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 205 | °C | |
| Middle Temperature | 180 - 205 | °C | |
| Front Temperature | 180 - 205 | °C | |
| Nozzle Temperature | 185 - 210 | °C | |
| Processing (Melt) Temp | 185 - 210 | °C | |
| Mold Temperature | 10.0 - 55.0 | °C | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 100 - 200 | rpm |
| Extrusion instructions |
|---|
| Spiral Flow Ratio, DSM Method: 3 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCUDIA® HDPE 5502E | REPSOL | HDPE, HMW | ALCUDIA® HDPE |
| ESPRENE EPDM 532 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Keldax® 6798 | DuPont Packaging & Industrial Polymers | Ethylene Copolymer | Keldax® |
| MAJORIS CG100 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| PENTAMID A GV30 H natur | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |