Kingfa PBT RG002
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MHlDyS_Kingfa-PBT-RG002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PBT RG002 is a polybutene terephthalate (PBT) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PBT RG002 are:
The typical application fields of Kingfa PBT RG002 are: electrical/electronic applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 1.1 | % | ASTM D955 |
| Transverse flow : 23°C | 1.6 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 48.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2000 | MPa | ASTM D790 |
| Flexural Strength 3 | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 510 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 108 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 81.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.700 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 230 - 255 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temperature Limit: 265°C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® RP223-60 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| Menzolit® SMC 0410 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| NEXUS PP HPP2 | Nexus Resin Group, LLC. | PP Homopolymer | NEXUS PP |
| FERREX® GPP20CS75HB | Ferro Corporation | PP, Unspecified | FERREX® |
| KEBAFORM® C 90 M | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |