Kepital® F30-52G
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | KEP Americas |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MHXyH4_KepitalF3052G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A UV-stabilized and gloss-reduced low-viscosity grade for general injection molding. Modified with a weather-resistant and gloss-reducing substance. Suitable for applications requiring superior weather resistance and low-gloss characteristics |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| shrinkage- Flow 1(3.00 mm) | 2.0 | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress (23°C) | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 88.0 | °C | ISO 75-2/A |
| Melting Temperature | 165 | °C | ISO 11357-3 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 19 | kV/mm | IEC 60243-1 |
| Note Message | |
|---|---|
| 1 . | 100mm diameter |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594B-G80E-M | TSRC Corporation | SEBS | T-Blend® |
| Vi-Chem PVC V130-61FR | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| ExxonMobil™ PP7694E2 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Elastron® G G301.A45.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Hifax HSBM CB 1158 G | LyondellBasell Industries | PP Impact Copolymer | Hifax |