Queo™ 0207LA
| Category: | Plastomer , Ethylene-based Plastomer |
| Manufacturer: | Borealis AG |
| Trademark: | Queo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MHTY34_Queo-0207LA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Queo™ 0207LA is an ethylene based octene plastomer produced in a solution polymerisation process using a metallocene catalyst. Additives Queo 0207LA contains a low amount of processing stabilizer. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.902 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.6 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Compression Molded) | 22.0 | MPa | ISO 527-2/5A |
| Tensile Strain (Break, Compression Molded) | 940 | % | ISO 527-2/5A |
| Flexural Modulus (Compression Molded) | 77.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Melting Temperature (DSC) | 96.0 | °C | ISO 11357 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® FR515 BK507 | DuPont Performance Polymers | PET | Rynite® |
| WELLAMID Nylon 6000 SCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Tritan™ TX1500HF | Eastman Chemical Company | Copolyester | Tritan™ |
| Karina WHITE PVC COMPOUND 800-10/10-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 08225 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |