Kingfa HG-235
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MH5NGw_Kingfa-HG-235.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa HG-235 is a polypropylene material, which contains a 20% filler. This product is available in North America or Asia Pacific,. The main features of Kingfa HG-235 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.3 - 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 80 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 1580 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 46 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm, injection molding | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm, injection molding | 73.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Filler Content, ISO3451/1, Method A: 20% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sympoxy™ 1225/561 | Hapco Inc. | Epoxy | Sympoxy™ |
| Fiberfil® J-60/20/E4 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Fortron® 1140L4 | Celanese Corporation | PPS | Fortron® |
| HAIPLEN EP60 T5 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| LEXAN™ PC1800 resin | SABIC Innovative Plastics | PC | LEXAN™ |