LNP™ THERMOCOMP™ PF008S compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MGhEph_LNP-THERMOCOMP-PF008S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound PF-1008 HS Product reorder name: PF008S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.98 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12700 | MPa | ASTM D638 |
| -- | 13000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 184 | MPa | ASTM D638 |
| Break | 186 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.3 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 9260 | MPa | ASTM D790 |
| -- | 9530 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 279 | MPa | ASTM D790 |
| -- | 278 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 92 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 25.1 | J | ASTM D3763 |
| -- | 21.6 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 196 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 208 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANCAR® 2865 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Trovicel® 19/24 mm | Röchling Engineering Plastics SE & Co. KG | PVC, Flexible | Trovicel® |
| WMB 126S | Pooya Polymer Tehran | Polyolefin, Unspecified | WMB |
| TYNEA 4250 | Tyne Plastics LLC. | Acetal (POM) Copolymer | TYNEA |
| ACCUTECH™ CP0436C30L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |