ResMart Ultra POM
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | ResMart |
| Trademark: | ResMart Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MGOmAE_ResMart-Ultra-POM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High performance copolymer polyacetal |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.6 - 2.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1500 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 116 - 121 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 182 - 218 | °C | |
| Mold Temperature | 79.4 - 107 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Dew Point: -25°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFLAME POLYPROPYLENE 10% TALC V2 | RIALTI Srl | PP Homopolymer | RIALFLAME |
| Wellamid® GS25-66 22L-N | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Borealis PP EH105AEB | Borealis AG | TPO | Borealis PP |
| Celanex® 2300 GV3/20 | Celanese Corporation | PBT | Celanex® |
| Clariant PBT PBT-1100G30TF15 | Clariant Corporation | PBT | Clariant PBT |