Order Products : sales@su-jiao.com
Matrixx 50S5202
| Category: | PC , Polycarbonate |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MDVQsV_Matrixx-50S5202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Matrixx 50S5202 is a polycarbonate (PC) material, which contains a 20% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The main characteristics of Matrixx 50S5202 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 - 0.30 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 96.5 | MPa | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| RTI | 93.3 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 282 - 310 | °C | |
| Middle Temperature | 282 - 310 | °C | |
| Front Temperature | 282 - 310 | °C | |
| Processing (Melt) Temp | 293 - 321 | °C | |
| Mold Temperature | 71.1 - 104 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 75 | rpm | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| -20°F Dewpoint |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7610 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SHIN-A SAP-4606XB60 | SHIN-A T&C | Acrylic, Unspecified | SHIN-A |