UmaPET MO

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MCGECy_UmaPET-MO.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KEY FEATURES

Uma PET MO is one side matte film with other side plain surface for excellent print quality.

Other side corona or chemical coating as optional for improved adhesion performance.

It has medium Haze, Medium gloss gloss film with excellent muted and grainy surface on matte side.

The film exhibits excellent thermal, mechanical and medium matte surface properties one side with normal surface on the other side.

It has excellent dimensional stability and excellent process ability. After metallization, shows silver finish as aesthetic.

APPLICATIONS

Excellent for packaging applications where plain side gives excellent print quality and other side matte finish to the print image.

While pouching or packing shows excellent thermal stability.

Typical end uses like soap wraps, baby wipes, moist tissues, dry fruits and other high endpackaging for different food / non - food products etc.

General Information
Features	Excellent Printability Good Adhesion Good Dimensional Stability Good Processability Good Thermal Stability Medium Gloss Metallizable
Uses	Film Packaging
Appearance	Matte Finish
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0120 mm	2.0	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction ¹			ASTM D1894
vs. Itself - Dynamic	0.38
vs. Itself - Static	0.42

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	12	µm
Film Thickness - Recommended / Available	12 µm
Tensile Strength			ASTM D882
MD : Break, 12 µm	196	MPa
TD : Break, 12 µm	206	MPa
Tensile Elongation			ASTM D882
MD : Break, 12 µm	90	%
TD : Break, 12 µm	90	%
Yield (12.0 µm)	59.5	m²/kg	Internal Method

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension - Plain side (12.0 µm)	44	dyne/cm	ASTM D2578

Optical	Nominal Value	Unit	Test Method
Gloss			ASTM D2457
60°, 12.0 µm, High Gloss Surface	110
60°, 12.0 µm, Matte Surface	45
Haze (12.0 µm)	35	%	ASTM D1003

Note Message
1 .	12 µm

Resin Grade	Manufacturer	Category	Trademark
VINIKA® D6228	Mitsubishi Chemical Performance Polymers, Inc.	PVC, Rigid	VINIKA®
Axiall PVC 1851 Clear 7002	Axiall Corporation	PVC, Flexible	Axiall PVC
Garaflex™ O 9940SA NAT	AlphaGary	TPE	Garaflex™ O
Hyflon® PFA P7310	Solvay Specialty Polymers	PFA	Hyflon® PFA
Sylvin 5210-75 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin