Versalloy™HC 9220-70 is a TPV alloy with strong fluidity and surface aesthetic effects, suitable for a variety of applications. Very strong coloring ability It can be bonded to polypropylene by overlapping molding Excellent surface aesthetics

General Information
Features	Non-phthalate plasticizer Recyclable materials Workability, good Good coloring Excellent appearance
Uses	overmolding Pipe fittings Soft touch application Soft handle Medical/nursing supplies
Agency Ratings	ISO 10993 Part 4 ISO 10993 Part 5 USP Class VI
RoHS Compliance	RoHS compliance
Appearance	Natural color
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.950	g/cm³	ASTM D792
Molding Shrinkage			ISO 294-4
Vertical flow direction	1.9	%	ISO 294-4
Flow direction	2.4	%	ISO 294-4

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	70		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ASTM D412
Transverse flow : 100% strain, 21°C	2.52	MPa	ASTM D412
Flow : 100% strain, 21°C ²	3.72	MPa	ASTM D412
Tensile Strength			ASTM D412
Transverse flow : Fracture, 21°C	4.05	MPa	ASTM D412
Flow : fracture, 23°C	4.81	MPa	ASTM D412
Tensile Elongation			ASTM D412
Transverse flow : fracture, 23°C	290	%	ASTM D412
Flow : Fracture, 21°C	240	%	ASTM D412
Tear Strength			ASTM D624
Transverse flow	36.4	kN/m	ASTM D624
Flow	36.4	kN/m	ASTM D624
Compression Set			ASTM D395B
23°C, 22 hr	17	%	ASTM D395B
23°C, 168 hr	18	%	ASTM D395B
70°C, 22 hr	41	%	ASTM D395B
70°C, 168 hr	42	%	ASTM D395B
100°C, 22 hr	51	%	ASTM D395B
100°C, 168 hr	62	%	ASTM D395B

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 11200 sec^-1)	18.7	Pa·s	ASTM D3835

Additional Information
Versalloy™ HC 9220-70 can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.Municipality waste stream recycle code is "7" which is designated for "Other".Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.

Additional Information

Versalloy™ HC 9220-70 can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.Municipality waste stream recycle code is "7" which is designated for "Other".Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	3.0	hr
Suggested Max Regrind	20	%
Rear Temperature	177 - 193	°C
Middle Temperature	182 - 218	°C
Front Temperature	193 - 224	°C
Nozzle Temperature	193 - 224	°C
Mold Temperature	15.6 - 26.7	°C
Back Pressure	0.00 - 0.689	MPa
Screw Speed	50 - 100	rpm

Injection instructions
以聚丙烯 (PP) 为基础的色母料最适合 Versalloy™ HC 9220-70 着色。使用熔体流动速率较高（范围为 25 - 40 克/10 分钟）的色母料，则能达到较好的颜色分散效果。典型的色母料用量为 1% 至 5%（重量）。不应采用以 PVC 为基础的色母料。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versalloy™ HC 9220-70 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Versalloy™ HC 9220-70 具有良好的熔体稳定性。如果机器闲置十五 (15) 分钟或以上，则应将机筒排空。注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：300 - 700 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒

Injection instructions

以聚丙烯 (PP) 为基础的色母料最适合 Versalloy™ HC 9220-70 着色。使用熔体流动速率较高（范围为 25 - 40 克/10 分钟）的色母料，则能达到较好的颜色分散效果。典型的色母料用量为 1% 至 5%（重量）。不应采用以 PVC 为基础的色母料。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versalloy™ HC 9220-70 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Versalloy™ HC 9220-70 具有良好的熔体稳定性。如果机器闲置十五 (15) 分钟或以上，则应将机筒排空。注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：300 - 700 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒

Extrusion	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	3.0	hr
Cylinder Zone 1 Temp.	166 - 182	°C
Cylinder Zone 2 Temp.	177 - 204	°C
Cylinder Zone 3 Temp.	182 - 216	°C
Die Temperature	182 - 210	°C

Note Message
1 .	2 hr
2 .	Mouth die c

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versalloy™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MCCE2v_Versalloy-HC-9220-70.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TEKAMID™ TB130GM	Mando Advanced Materials Co., Ltd.	Nylon 6	TEKAMID™
VALOX™ 420 resin	SABIC Innovative Plastics	PBT	VALOX™
APEX® 71-2401-A	Teknor Apex Company	PVC, Flexible	APEX®
DeWAL DW 404BNC	DeWAL Industries	UHMWPE	DeWAL
Karina CLEAR PVC COMPOUND -E 80/200-SI-CRMT	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina