RESOLE FM 4008
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | RESOLE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MC4vh6_RESOLE-FM-4008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 4008 is a fiberglass and mineral reinforced phenolic resole compound, with excellent dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 50.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 14000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 140 | MPa | ASTM D790 |
| Compressive Strength | 240 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 265 | °C | ASTM D648 |
| CLTE - Flow | 1.9E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | 180 | sec | ASTM D495 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ASTM properties listed were tested in accordance with ASTM D5948.Powder Density, ASTM D1895: 0.8 g/cm³Water Absorption, ASTM D570, 48 hrs, 50°C: 0.35%DTUL @264psi - Unannealed, ASTM D648, Post Baked, Compression Molded: >282°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Desmopan® DP 3055D | Covestro - PUR | TPU-Polyester | Desmopan® |
| Gallonprene® GP520-7501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Huafon EP127 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| LEXAN™ 203R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LEXAN™ 143 resin | SABIC Innovative Plastics | PC | LEXAN™ |