Bormed SC820CF is a very soft random heterophasic copolymer. This grade is suitable for the manufacturing of tubular water quenched films and unoriented films on chill roll process. |
General Information | |
---|---|
Features |
|
Uses |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.9 | g/10 min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Flexural Modulus (23°C, Injection Molded) | 550 | MPa | ISO 178 |
Coefficient of Friction | > 0.70 | ISO 8295 |
Films | Nominal Value | Unit | Test Method |
---|---|---|---|
Film Thickness - Tested | 50 | µm | |
Tensile Modulus | ISO 527-3 | ||
MD : 50 µm | 330 | MPa | |
TD : 50 µm | 330 | MPa | |
Tensile Strength | ISO 527-3 | ||
MD : 50 µm | 50.0 | MPa | |
TD : 50 µm | 50.0 | MPa | |
Tensile Elongation | ISO 527-3 | ||
MD : Break, 50 µm | 650 | % | |
TD : Break, 50 µm | 670 | % | |
Instrumented Dart Impact (50 µm, Total Energy) | 30.0 | J | ISO 7765-2 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Melting Temperature | 141 | °C | ISO 11357-3 |
Optical | Nominal Value | Unit | Test Method |
---|---|---|---|
Gloss (20°, 50.0 µm) | > 120 | ASTM D2457 | |
Haze (50.0 µm) | < 1.0 | % | ASTM D1003 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
ResinDirect COPPI20 | ResinDirect | PP Copolymer | ResinDirect |
ResMart Ultra SAN 9 | ResMart | SAN | ResMart Ultra |
GAPEX® HP RPP30EC17WH | Ferro Corporation | PP Homopolymer | GAPEX® HP |
Karina BLACK PVC COMPOUND 70900-48/ 1-F-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
MAJORIS BG304 | AD majoris | PP, Unspecified | MAJORIS |