IROGRAN® A 60 E 4902
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MAyp6d_IROGRAN-A-60-E-4902.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 60 E 4902 is a soft, high performance polyester based thermoplastic polyurethane intended for extrusion and moulding applications. IROGRANA 60 E 4902 is part of the HUNTSMAN Film and Sheet and Injection-Moulding product ranges. It is processable at low temperatures and offers a specially designed, flexible material suitable for elastic films & mouldings. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.14 | g/cm³ | ASTM D792, DIN 53478 |
| Melt Volume-Flow Rate (MVR) (160°C/8.7 kg) | 35.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, Injection Molded | 56 | ASTM D2240 | |
| Shore D, Injection Molded | 15 | ASTM D2240, DIN 53505 | |
| Shore A, Injection Molded | 55 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | |||
| -- | 43 | mm³ | DIN 53516 |
| -- | 43 | mm³ | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High : 635.0 µm | 145 | °C | |
| Low : 635.0 µm | 110 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set 4(200% Strain) | 8 | % | ASTM D412, DIN 53504 |
| Tensile Stress 5 | |||
| 100% Strain, 0.635 mm | 2.34 | MPa | ASTM D412 |
| 100% Strain, 0.635 mm | 1.40 | MPa | DIN 53504 |
| 300% Strain, 0.635 mm | 4.07 | MPa | ASTM D412 |
| 300% Strain, 0.635 mm | 2.40 | MPa | DIN 53504 |
| Tensile Strength 6 | |||
| Break, 0.635 mm | 7.52 | MPa | ASTM D412 |
| Break, 0.635 mm | 10.0 | MPa | DIN 53504 |
| Tensile Elongation 7 | |||
| Break, 0.635 mm | 720 | % | ASTM D412 |
| Break, 0.635 mm | 900 | % | DIN 53504 |
| Tear Strength 8 | |||
| 0.635 mm | 35.9 | kN/m | ASTM D624 |
| 0.635 mm | 25 | kN/m | DIN 53515 |
| Compression Set 9 | |||
| 23°C, 70 hr | 40 | % | ASTM D395 |
| 70°C, 24 hr | 80 | % | ASTM D395 |
| 23°C, 70 hr | 35 | % | DIN 53517 |
| 70°C, 24 hr | 60 | % | DIN 53517 |
| Bayshore Resilience | 60 | % | ASTM D2632 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 98.9 to 130 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 40.0 | °C | |
| Drying Time - Hot Air Dryer | 4.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 160 to 171 | °C | |
| Middle Temperature | 160 to 171 | °C | |
| Front Temperature | 160 to 171 | °C | |
| Nozzle Temperature | 160 to 171 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 160 to 171 | °C | |
| Cylinder Zone 2 Temp. | 160 to 171 | °C | |
| Cylinder Zone 3 Temp. | 160 to 171 | °C | |
| Cylinder Zone 4 Temp. | 160 to 171 | °C | |
| Cylinder Zone 5 Temp. | 160 to 171 | °C | |
| Adapter Temperature | 160 to 171 | °C | |
| Die Temperature | 160 to 171 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Extruded Film, 0.025 in |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Extruded Film |
| 8 . | Extruded Film |
| 9 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3940C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TAROLOX 10 G3 | Taro Plast S.p.A. | PBT | TAROLOX |
| Ethylplus 029/UV BLACK | Fainplast Compounds S.r.l | LDPE | Ethylplus |
| DuraFlex 826 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| KOPLA PA6 KRE1010 | KOPLA Co., Ltd. | Nylon 6+ABS | KOPLA PA6 |