YUNGSOX® PP 1009
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Formosa Polypropylene |
| Trademark: | YUNGSOX® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MAYrUM_YUNGSOX-PP-1009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
YUNGSOX® PP 1009 is a Polypropylene Homopolymer (PP Homopolymer) material. It is available in Asia Pacific. Important attributes of YUNGSOX® PP 1009 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.3 to 1.7 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 34.3 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 300 | % | ISO 527-2 |
| Flexural Modulus | 1320 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 152 | °C | ISO 306 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E190L | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Sinvicomp SIF4569 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sylvin 7868-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Armlen® PP SM 20-1UP | Poly Plastic | PP, Unspecified | Armlen® |
| ESENTTIA 08H85DB-BC | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |