SAXALAC™ 108GF17
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MA7VyX_SAXALAC-108GF17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Saxalac 108 GF17 is a 17% glasfibres reinforced ABS injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.60 | % | ISO 294-4 |
| Moisture Content 1 | < 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6300 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 18 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 60.0 mm Span) | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 104 | °C | ISO 306/B50 |
| Ball Pressure Test (98°C, 2.00 mm) | Pass | IEC 60335-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | B130 |
| 2 . | 80x10x4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC KL 95 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| HiFill® PA12 E HS | Techmer Engineered Solutions | Nylon 12 | HiFill® |
| KumhoSunny PA/PPE HAP8720G | Shanghai KumhoSunny Plastics Co., Ltd. | Nylon+PPE | KumhoSunny PA/PPE |
| InnoPlus HD6366M | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Karina WHITE PVC COMPOUND E 854-10/144-ERYM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |