Adflex X 500 F is a thermoplastic polyolefin which has been developed for co-extruded cast film and injection moulding applications. Adflex X 500 F features a high softness, a low modulus, high gloss and excellent clarity. It has been especially developed as central layer of tough transparent co-extruded cast-film structures. It can be blended with other transparent polyolefinic resins to improve the low temperature impact resistance maintaining the transparency of the film. Adflex X 500 F can be processed on conventional PP cast film lines. It is also suited for injection moulding applications where high transparency and good gloss combined with good flexibility is required like e.g. housewares and toys. It does not contain any slip nor anti-blocking agents. For regulatory information please refer to Adflex X 500 F Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 14.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 500 | % | ISO 527-2 |
| Flexural Modulus | 470 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 14 | kJ/m² | |
| -20°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | > 60 | ASTM D2457 | |
| Haze (50.0 µm) | 13 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8071-82 WHITE 1148 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unipren® Elastomers B3 NTLA010 35A UP308 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Lucon® CP6059F | LG Chem Ltd. | PC | Lucon® |
| EPAMOULD 650D12 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| LNP™ FARADEX™ AS003 compound | SABIC Innovative Plastics | ABS | LNP™ FARADEX™ |