Pearlbond™ 501
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlbond™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M9VlB3_Pearlbond-501.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEARLBOND® 501 is a linear, polycaprolactone-copolyester polyurethane, supplied in form of white spherical granules with a high crystallization rate and a very high thermoplasticity level. Pearlbond® 501 can be added to formulations of REACTIVE POLYURETHANE HOT-MELTS (HMPUR), in order to improve the crystallisation speed. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (20°C) | 1.19 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 30 to 60 | g/10 min | ISO 1133 |
| Moisture Content | < 1500 | ppm | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Rate | 15.0 to 17.0 | min | Internal Method |
| OH Value | < 3.00 | mg KOH/g | Internal Method |
| Thermoplasticity | Very High | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 63.0 to 67.0 | °C | Internal Method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (130°C) | 950 | Pa·s | ISO 1133 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-403-M-G30 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Cosmic DAP K61/6230 | Cosmic Plastics, Inc. | DAP | Cosmic DAP |
| Elastron® D D400.A50.T | Elastron USA, Inc. | SBS | Elastron® D |
| Latiohm 66-10 H2 CNT G/35 | LATI S.p.A. | Nylon 66 | Latiohm |
| Microthene® MP625962 | LyondellBasell Industries | LLDPE | Microthene® |