LNP™ THERMOCOMP™ ZFM3314 compound
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M8qeWR_LNP-THERMOCOMP-ZFM3314-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
glass, mineral filled PPE Also known as: LNP* THERMOCOMP* Compound ZFM3314 Product reorder name: ZFM3314 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5800 | MPa | ISO 178 |
| Flexural Stress | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 170 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 179 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 8.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Nozzle Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3674 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SUPREME Specialty PS SP564 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| Catalyst CT/5 UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Colorite CS Series CS9040UL-85B | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Hostacom XBR 169 G C12463 | LyondellBasell Industries | PP Copolymer | Hostacom |