Badamid® PPA CF30
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M7wplG_BadamidPPACF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Heat stabilized 30% carbon fibres reinforced injection moulding grade based on a partly aromatic Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 2.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.80 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 26500 | 25500 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 260 | 220 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 1.3 | 1.8 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | 10 | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 295 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 285 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 313 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | DIN 53752 | |||
| Flow | 3.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Lateral | 6.0E-5 | -- | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 60216 | |||
| -- | 270 | -- | °C | IEC 60216 |
| -- 5 | 180 | -- | °C | IEC 60216 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.8 mm | HB | -- | UL 94 | |
| 1.6 mm | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 330 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 10 K/min |
| 5 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC5UVZ (Series: UV/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| AQUAFORCE® PA66 G30-01 SCHWARZ | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | AQUAFORCE® |
| Ateva® 9030 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Axiall PVC 9175 J Clear 38 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Sylvin 916VO-70C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |