Arylmax® K7500CF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Arylmax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M6szq0_Arylmax-K7500CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arylmax® K7500CF30 is a Polyaryletherketone (PAEK) product filled with 30% carbon fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 23000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 260 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 20000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 370 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 170 | °C | DSC |
| Melting Temperature | 353 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 380 | °C | |
| Middle Temperature | 380 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 380 | °C | |
| Mold Temperature | 200 to 210 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Boda BDF-H2751 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| EUROPLEX® Sheet PPSU 99470 Transparent | Evonik Industries AG | PPSU | EUROPLEX® Sheet |
| Garaflex™ E 89-086-C3 NAT NF LCF-R | AlphaGary | TPE | Garaflex™ E |
| MAJORIS FC185C - 1298 | AD majoris | PP, Unspecified | MAJORIS |
| DAI-EL™ G-551 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |