Diakon® TD525
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M5M0DL_Diakon-TD525.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diakon® TD525 is a Polymethyl Methacrylate Acrylic material. It is available in Europe for injection molding. Primary attribute of Diakon® TD525: Flame Rated. Typical application of Diakon® TD525: Automotive |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 1.9 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.80 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 60 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 20 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 38 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 3.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ISO 306/A |
| -- | 101 | °C | ISO 306/B |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index | 650 | °C | IEC 60695-2-12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Hopper Temperature | 50.0 to 80.0 | °C | |
| Rear Temperature | 190 to 240 | °C | |
| Middle Temperature | 210 to 260 | °C | |
| Front Temperature | 210 to 280 | °C | |
| Nozzle Temperature | 220 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2645 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| STAR-THERM® E B-2C | EPIC Polymers | Nylon 6 | STAR-THERM® |
| Nanjing Hongrui PP P860 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| ESPOLEX 901 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| KumhoSunny AES HW602HF | Shanghai KumhoSunny Plastics Co., Ltd. | AES | KumhoSunny AES |