LNP™ STAT-KON™ WE002 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M4dA66_LNP-STAT-KON-WE002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* WE002 is a compound based on PBT resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound WC-1002 Product reorder name: WE002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.35 | g/cm³ | ASTM D792 |
| -- | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 to 1.1 | % | ASTM D955 |
| Across Flow : 24 hr | 0.91 to 1.1 | % | ISO 294-4 |
| Flow : 24 hr | 0.39 to 0.56 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.092 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.11 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10100 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 133 | MPa | ASTM D638 |
| Break | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.5 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7390 | MPa | ASTM D790 |
| -- | 7760 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 181 | MPa | ASTM D790 |
| -- | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 4.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.07 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 208 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 201 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 K TFE 15 | RTP Company | PARA | RTP |
| Tenite™ Propionate 376E4000012 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Braskem PP RP 250 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| GERMAMID 6.6 ST SCHWARZ | Kunststoff-Kontor-Hamburg GmbH | Nylon 66 | GERMAMID |
| KumhoSunny PC 3601 | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |