TAIRILAC AG10NP
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRILAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M3oX4O_TAIRILAC-AG10NP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC ABS resin AG10NP meets the requirements of SGS, CSA, NSF and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class R, 23°C | 105 | ASTM D785 | |
| R scale, 23°C | 105 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 46.1 | MPa | ASTM D638 |
| 23°C | 46.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2450 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 73.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 430 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648, ISO 75-2/A | ||
| 1.8 MPa, unannealed, 12.7mm | 88.0 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, annealed 1 | 98.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 101 | °C | ISO 306/A, ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Die Temperature | 190 - 230 | °C |
| Extrusion instructions |
|---|
| Screw Temperature: 180 to 230°CCooling Roll - Upper: 70 to 80°CCooling Roll - Middle: 80 to 90°CCooling Roll - Lower: 90 to 110°C |
| Note Message | |
|---|---|
| 1 . | 85°Cx8Hr |
| 2 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® CB5108 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| SUMIPEX® MHF | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| Vatpol 300 | Vatan Plastik San. Tic. AS | PE, Unspecified | Vatpol |
| DENKA EVA TEX 82 | Denka Company Limited | EVA | DENKA EVA TEX |
| Polygen SC75C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |