UmaPET EMML

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	M26nkO_UmaPET-EMML.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KEY FEATURES

Uma PET EMML is metallized film with metal deposition on emboss able surface. This film exhibits excellent process ability and is suitable for high speed and high resolution hard embossing. The emboss able surface eliminates the need for additional polymer coating over film.

It has excellent mechanical properties, flex crack resistance and excellent gloss.

APPLICATIONS

Uma PET EMML film is mostly used as embossing film for making Holographic Film in different holographic textures which is used in wide range of applications.

Packaging for making pouches, paper lamination and other decorative end use.

Security stickers, stickers etc as deterrent for duplication and counterfeiting of products such as credit cards drivers licenses, pharmaceutical products, computer software etc.

General Information
Features	Embossed Good Crack Resistance Good Processability High Gloss Metallizable
Uses	Film Packaging Stationary Supplies
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0130 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0130 mm	0.40	%
Surface Tension - Metallized side (13.0 µm)	56	mN/m	ASTM D2578

Films	Nominal Value	Unit	Test Method
Yield (12.0 µm)	55.0	m²/kg	Internal Method

Optical	Nominal Value	Unit	Test Method
Optical Density (13.0 µm)	-3.6 to 6.4	%	Internal Method

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	13	µm
Film Thickness - Recommended / Available	13 µm
Tensile Strength			ASTM D882
MD : Break, 13 µm	206	MPa
TD : Break, 13 µm	216	MPa
Tensile Elongation			ASTM D882
MD : Break, 13 µm	100	%
TD : Break, 13 µm	90	%
Oxygen Permeability ¹(23°C, 13 µm)	< 1.80	cm³/m²/24 hr	ASTM D3985
Water Vapor Transmission ²	< 1.5	g/m²/24 hr	ASTM F1249

Note Message
1 .	0%RH
2 .	37.8°C, 90%RH, 13 µm

Resin Grade	Manufacturer	Category	Trademark
SCHULAMID® 66GF25	A. Schulman Inc.	Nylon 66	SCHULAMID®
ACCUTECH™ CP0436M30CL	ACLO Compounders Inc.	PP Copolymer	ACCUTECH™
Braskem PE SLL218/21	Braskem	LLDPE	Braskem PE
LAPEROS® S471	Polyplastics Co., Ltd.	LCP	LAPEROS®
POCAN® BF 4222 000000	LANXESS Corporation	PBT	POCAN®