Adiprene® LFP 950A
| Category: | PUR-Ether/PPDI , Polyurethane (Polyether, PPDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M212xw_Adiprene-LFP-950A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADIPRENE LFP 950A is a PPDI-terminated polyether prepolymer with very low free PPDI content (typical < 0.1%) for easier management of health and safety during handling. ADIPRENE LFP 950A yields a high performance 95-97 Shore A hardness elastomer when cured with VIBRACURE® A 250. The high performance features of ADIPRENE LFP 950A are due to PPDI (p-phenylene diisocyanate), a special building block that imparts exceptional properties to cast polyurethane elastomers. The unique combination of properties exhibited by PPDI-based prepolymers is superior to those available from standard prepolymers based on TDI or MDI. Features of ADIPRENE LFP 950A include:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 to 97 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% Strain | 4.48 | MPa | |
| 10% Strain | 8.62 | MPa | |
| 15% Strain | 12.4 | MPa | |
| 20% Strain | 15.9 | MPa | |
| 25% Strain | 20.7 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 12.8 | MPa | |
| 300% Strain | 15.5 | MPa | |
| Tensile Strength | 47.6 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 570 | % | ASTM D412 |
| Tear Strength (Split) | 23 | kN/m | ASTM D470 |
| Compression Set | ASTM D395B | ||
| 70°C, 22 hr | 38 | % | |
| 100°C, 22 hr | 48 | % | |
| Bayshore Resilience | 57 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life (80°C) | 4.0 | min | |
| Demold Time | > 30 | min | |
| Post Cure Time (116°C) | 16 | hr |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Dynamic Properties | |||
| Storage Modulus : 30°C | 5.64E+8 | dynes/cm² | |
| Storage Modulus : 150°C | 4.40E+8 | dynes/cm² | |
| Tangent Delta : 30°C | 0.0150 | ||
| Tangent Delta : 150°C | 0.0190 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP CPC35C | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PP |
| Cellophane™ 340 Rayo M | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Chemical Resources PMMA600 | Chemical Resources, Inc. | Acrylic (PMMA) | Chemical Resources |
| Monprene® CP-29451 XRD (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Wanthane® WHT-56170 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |