Beetle X/Z, ZXT
| Category: | Urea Formald , Urea Formaldehyde |
| Manufacturer: | BIP (Oldbury) Limited |
| Trademark: | Beetle |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LzD7mB_Beetle-X-Z-ZXT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Wet granulated grade. As these grades are less "gassy" than dry granulated materials they are particularly suitable for thick section mouldings such as toilet seats. They are also recommended for moulding closures because their fines free flowing powder properties allow accurate metering of very small charge weights. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Bulk Factor | 2.2 | ISO 171 | |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.73 | % | |
| -- 2 | 0.76 | % | |
| Water Absorption | |||
| Cold 3 | 195.0 | mg | DIN 53472 |
| Cold 4 | 62.0 | mg | ISO 62 |
| Hot 5 | 280.0 | mg | ISO 62 |
| Post Shrinkage | ISO 2577 | ||
| -- 6 | 0.50 | % | |
| -- 7 | 0.50 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 120 | °C | DIN 43458 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Stress | 99.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 2.1 | kJ/m² | ISO 180/C |
| Unnotched Izod Impact Strength | 8.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 133 | °C | ISO 75-2/Ae |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | DIN 53483 |
| Volume Resistivity | 1.0E+12 | ohms·cm | DIN 53483 |
| Electric Strength | IEC 60243-1 | ||
| -- 8 | 8.9 | kV/mm | |
| -- 9 | 7.2 | kV/mm | |
| Dissipation Factor | 0.025 | DIN 53483 | |
| Comparative Tracking Index | > 600 | V | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Oxygen Index 10 | 33 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Preheated powder |
| 2 . | Cold powder |
| 3 . | 96 hr @ 23°C |
| 4 . | 24 hr @ 23°C |
| 5 . | 30 min @ 100°C |
| 6 . | Cold powder |
| 7 . | (48 hr) Preheated powder |
| 8 . | (90°C) Preheated powder |
| 9 . | Cold powder |
| 10 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V929-03 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Royalite R26 | Spartech Plastics | ABS | Royalite |
| Elastron® G G300.D50.N | Elastron USA, Inc. | SEBS | Elastron® G |
| LEXAN™ HP4 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| PIVINEL™ JYY-HARD2 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |