MERICAN® 9190P

Category:	Polyester Alloy , Polyester Alloy
Manufacturer:	Huachang Polymer Co., Ltd.
Trademark:	MERICAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Lz8gOY_MERICAN-9190P.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

MERICAN® 9190P is a prepromoted, low-viscosity unsaturated polyester resin, special designed for vacuum infusion and RTM process. It presents good weathering resistance( cold and hot alternate), water resistance, excellent mechanical properties and process performance. MERICAN 9190P comply with Germanischer Lloyd (GL) requirements for wind blade applications.

PROPERTY

Low-viscosity

Shorter geltime drift, good storage stability

Low peak exotherm, thick pieces can be formed at one time

Good curing properties, thoroughly curing for thin pieces

Excellent mechanical properties, good adhesion between laminates

Resistant to fatigue, aging and corrosion

APPLICATION

Suitable for the fabricatiion of composites products with high performance and complex structure, especially large windmill blades and yachts, etc.

Suitable for vacuum infusion process

General Information
Features	Fatigue Resistant Good Adhesion Good Corrosion Resistance Good Processability Good Weather Resistance Low Exotherm Low to No Water Absorption Low Viscosity
Uses	Engineering Parts
Appearance	Red
Processing Method	Resin Transfer Molding Vacuum Forming

Physical	Nominal Value	Unit	Test Method
Solids Content	55 to 60	%	ISO 2884

Thermal	Nominal Value	Unit	Test Method
Thermal Stability (80°C)	> 2	day

Thermoset	Nominal Value	Unit	Test Method
Gel Time (25°C)	> 2.0	hr	ISO 2535

Additional Information	Nominal Value	Unit	Test Method
Peak Exotherm ¹(25°C)	70 to 110	°C

Hardness	Nominal Value	Unit	Test Method
Barcol Hardness	45		ASTM D2583

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3400	MPa	ASTM D638, ISO 527-2
Tensile Stress
Yield	76.0	MPa	ISO 527-2
--	76.0	MPa	ASTM D638
Tensile Elongation (Break)	3.8	%	ASTM D638, ISO 527-2
Flexural Modulus	3800	MPa	ASTM D790, ISO 178
Flexural Strength	128	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	90.0	°C	ASTM D648, ISO 75-2/A

Thermoset	Nominal Value	Unit	Test Method
Thermoset Mix Viscosity (25°C)	100 to 200	cP	ISO 2555

Note Message
1 .	100 gm

Resin Grade	Manufacturer	Category	Trademark
Viton® A-100	DuPont Performance Elastomers	Fluorelastomer	Viton®
Yanshan PE LD104	SINOPEC Beijing Yanshan Petrochemical	LDPE	Yanshan PE
Generic API	Generic	API	Generic
ELIX™ ABS M203FC	ELIX Polymers, S. L.	ABS	ELIX™ ABS
LNP™ STAT-KON™ MD000IS compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ STAT-KON™