Stanyl® TE263F6
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LyzbA9_Stanyl-TE263F6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl® TE263F6 is a Polyamide 46 (Nylon 46) material filled with 30% glass fiber. It is available in North America. Important attributes of Stanyl® TE263F6 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.31 | -- | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 140 | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | 10 | % | ISO 527-2 |
| Flexural Modulus | 6300 | 3200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 15 | -- | kJ/m² | |
| 23°C | 20 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 280 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 295 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 8.0E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 305 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC2CF-2 | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Akoalit PB 4267 grey | LyondellBasell Industries | PB | Akoalit |
| Hanwha Total PP BJ750 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Escorene™ Ultra FL 01418 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Teldene® H06ML | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |