Vyncolit® BXE6952
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lys7a5_Vyncolit-BXE6952.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit BXE6952 is a glass fibre reinforced phenolic moulding compound with superior mechanical properties: very high tensile and flexural strength combined with high elongation at break. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.73 | g/cm³ | ISO 1183 |
| Apparent Density | 0.55 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.15 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 0.050 | % | ISO 62 |
| Post Shrinkage | 0.020 | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.6 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Type | PF 2 C3 | ||
| Pourability | Good |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 129 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 17000 | MPa | ISO 178 |
| Flexural Stress | 247 | MPa | ISO 178 |
| Compressive Stress | 300 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | TMA | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Transverse | 4.2E-5 | cm/cm/°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AZM-23-G9 | Arkema | Nylon 12 | Rilsan® |
| Rynite® FR530 NC010 | DuPont Performance Polymers | PBT | Rynite® |
| Axiall PVC SP-7221 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| PolyBlend™ 1100-55A | AdvanSource Biomaterials Corp. | TPU Alloy | PolyBlend™ |
| Hyflon® MFA® P6022 | Solvay Specialty Polymers | Perfluoropolymer | Hyflon® MFA® |