Kepital® FG2015
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LyDkwx_Kepital-FG2015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium viscosity grade for general injection molding. It was reinforced glass fiber, and so suitable for parts requiring very high stiffness, fatigue resistance, creep resistance, and heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 12 | g/10 min | ASTM D1238 |
| -- | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (2.00 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 111 | MPa | ASTM D638 |
| Break, 23°C | 120 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 3.0 | % | ASTM D638 |
| Break, 23°C | 3.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5350 | MPa | ASTM D790 |
| 23°C | 5200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 157 | MPa | ASTM D790 |
| 23°C | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 164 | °C | ASTM D648 |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® SE25CW | BASF Leuna GmbH | Nylon 66 | Miramid® |
| APEX® 1020 | Teknor Apex Company | PVC, Semi-Rigid | APEX® |
| Clariant Nylon 6/6 PA-113C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ELASTOSIL® R plus 4066/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Sinvicomp SSZ6309 KD11 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | SINVICOMP |