Torayca® 3101T-20V
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torayca® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ly4Z6s_Torayca-3101T-20V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torayca® 3101T-20V is a Polyamide 66 (Nylon 66) product filled with 20% carbon fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.90 | % | |
| Flow : 3.00 mm 2 | 0.30 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | % | |
| PV Limit - vs. S45C | 2.3 | MPa·m/s | Suzuki Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Amount of Wear - vs. S45C 3 | 0.700 | mg/hr | Suzuki Method |
| Coefficient of Friction - vs. S45C 4 | 0.320 | Suzuki Method | |
| Tensile Stress (23°C) | 223 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 13800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 310 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.1 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Melting Temperature | 265 | °C | DSC |
| CLTE - Flow | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 1MPa, 0.33 m/s |
| 4 . | 1MPa, 0.33 m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ N66-MOS3 BK | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| SABIC® PPcompound G3220A | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Tenac™ LT802 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| EnviroPCABS 5010IM | West Michigan Compounding | PC+ABS | EnviroPCABS |
| Jiangsu Sinarise EI9000X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |