Ultramid® A3EG10 FC Aqua
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lxas6C_Ultramid-A3EG10-FC-Aqua.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid® A3EG10 FC Aqua black is optimized for plastic parts, mandatory requiring material approvals for drinking water or direct food contact. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 8.00 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 0.82 | -- | % | ISO 294-4 |
| Flow direction | 0.33 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 3.7 - 4.3 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.0 - 1.4 | -- | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 130 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.45 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature index- at 50% loss of tensile strength | IEC 60216 | |||
| -- 2 | 135 | -- | °C | IEC 60216 |
| -- 3 | 165 | -- | °C | IEC 60216 |
| Maximum operating temperature- short cycle operation | 240 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | -- | FMVSS 302 | |
| Polymer Abbreviation | PA66-GF50 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16800 | 12500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 240 | 180 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.5 | % | ISO 527-2 |
| Tensile Creep Modulus 4(1000 hr) | -- | 7800 | MPa | ISO 899-1 |
| Flexural Modulus | 15000 | 13500 | MPa | ISO 178 |
| Flexural Stress | 360 | 300 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 18 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 95 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 13 | 15 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 5.0E-6 - 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 5.0E-5 - 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1300 | -- | J/kg/°C | |
| Thermal Conductivity | 0.37 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | 6.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.17 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 300 | °C | |
| Middle Temperature | 300 | °C | |
| Front Temperature | 300 | °C | |
| Nozzle Temperature | 300 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 80°C |
| 2 . | 20000 h |
| 3 . | 5000 h |
| 4 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8957-80 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VITAMIDE® AR33NT6520 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Aarolene® ARPS 100-2 | Aaron Industries Corp. | PS (MIPS) | Aarolene® |
| PENTAMID AB GK30 H natur | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| Nylux 66-GF33NAT | KMI Group, Inc. | Nylon 66 | Nylux |