DOW™ LLDPE DNDA-8320 NT 7

Category:	LLDPE , Linear Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LvEYeG_DOW-LLDPE-DNDA-8320-NT-7.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Injection molding

General purpose applications

Excellent low temperature impact strength, rigidity, stress crack resistance and processability

Very narrow molecular weight distribution

Complies with U.S. FDA 21 CFR 177.1520 (c)3.1a

Complies with EU, No 10/2011

Complies with U.S. FDA-DMF

Complies with CANADIAN HPFB NO OBJECTION (WITH LIMITATIONS)

Consult the regulations for complete details.

DOW DNDA-8320 NT 7 Linear Low Density Polyethylene (LLDPE) Resin is produced using the UNIPOL™ PE Process Technology and is intended for use in general purpose injection molding applications. This resin has been designed to have excellent impact strength, rigidity, environmental stress crack resistance and processability.

General Information
Agency Ratings	DMF not rated FDA 21 CFR 177.1520(c) 3.1a HPFB (Canada) No Objection 2 Europe No 10/2011
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.924	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	20	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50)	20.0	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	50		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	11.7	MPa	ASTM D638
Fracture	7.58	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	3.0	%	ASTM D638
Fracture	60	%	ASTM D638
Flexural Modulus - 2% Secant	386	MPa	ASTM D790B

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength ¹	168	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	42.8	°C	ASTM D648
Brittleness Temperature	< -76.1	°C	ASTM D746
Vicat Softening Temperature	93.9	°C	ASTM D1525
Melting Temperature (DSC)	123	°C	Internal method
Peak Crystallization Temperature (DSC)	108	°C	Internal method

Additional Information
根据 ASTM D 4976 进行基板模制和测试。

Note Message
1 .	Type s

Resin Grade	Manufacturer	Category	Trademark
XYRON™ 340V	Asahi Kasei Chemicals Corporation	PPE+PS	XYRON™
BCC Resins BC 5114	BCC Products Inc.	Epoxy	BCC Resins
Axiall PVC 18731	Axiall Corporation	PVC, Flexible	Axiall PVC
Eastar™ MN006 Natural	Eastman Chemical Company	Copolyester	Eastar™
PENTAMID A MK30 E H natural	PENTAC Polymer GmbH	Nylon 66	PENTAMID A