| Polyamide 6, medium viscosity, 30% glass fiber reinforced, heat stabilised, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 1.0 | % | |
| Flow : 23°C, 72 hr | 0.35 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.7 | % | |
| Equilibrium, 23°C, 50% RH 2 | 0.20 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Ash Content (650°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.6 | % | ISO 527-2/1A/20 |
| Flexural Modulus 3 | 7200 | MPa | ISO 178 |
| Flexural Stress 4 | 270 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 94 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 217 | °C | ISO 306/A50 |
| -- | 214 | °C | ISO 306/B50 |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(2.00 mm) | 40 | mm/min | ISO 3795 |
| Glow Wire Ignition Temperature | 650 | °C | VDE 0471/2 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| 2 . | 24 hrs |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7841-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SUPREME Specialty PS SP6415 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| TOTAL Polypropylene PPH 3827WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| NOVALAST® 8001 | NOVA Polymers, Inc. | TPV | NOVALAST® |
| ENVIROLOY® ENV15-NC540 | ENVIROPLAS®, Inc. | PC+ABS | ENVIROLOY® |