Order Products : sales@su-jiao.com
Kingfa PP-R001
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LustFi_Kingfa-PP-R001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PP-R001 is a Polypropylene material. It is available in Asia Pacific or North America. Important attributes of Kingfa PP-R001 are:
Typical application of Kingfa PP-R001: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.0 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 28.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 40 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 1800 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 30.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 51 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm, Injection Molded) | 125 | °C | ASTM D648 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.950 mm | V-0 | ||
| 1.50 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® MG-0050N | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| KOPLA PA6 KNE1030 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Latene® 7 TR-V2 | LATI S.p.A. | PP Homopolymer | Latene® |
| OTECH PVC OW837 GPT - Automotive Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Plaslube® PA6 GF20 RM BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |