PPC130M 9249 is a 30% mineral filled, stabilised polypropylene copolymer black compound intended for extrusion applications. It offers reasonable rigidity and high impact strength, combined with good service life durability over a wide temperature range.

General Information
Additive	heat stabilizer UV stabilizer
Features	Impact resistance, high Good UV resistance Good liquidity Excellent appearance
Appearance	Black
Forms	Particle
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	1.15	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	2.0	g/10 min	ISO 1133
Molding Shrinkage ¹	0.70 - 1.5	%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1600	MPa	ISO 527-2
Tensile Stress (Yield)	21.0	MPa	ISO 527-2
Tensile Strain			ISO 527-2
Yield	3.2	%	ISO 527-2
Fracture	> 150	%	ISO 527-2
Flexural Modulus	1750	MPa	ISO 178
Flexural Stress	30.0	MPa	ISO 178
Bending strain- at peak stress	5.0	%	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	40	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	120	°C	ISO 75-2/B
1.8 MPa, not annealed	75.0	°C	ISO 75-2/A
Melting Temperature	169	°C	DSC

Flammability	Nominal Value		Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB		UL 94

Extrusion	Nominal Value	Unit
Drying Temperature	< 60.0	°C
Cylinder Zone 1 Temp.	190 - 220	°C
Cylinder Zone 2 Temp.	190 - 220	°C
Cylinder Zone 3 Temp.	190 - 220	°C
Die Temperature	190 - 220	°C

Extrusion instructions
Maximum Melt temperature 230°CPP materials are not hygroscopic and drying should not normally be necessary.If surface moisture is present on the granules, drying is permissible but temperature should not exceed 60°C to avoid risk of agglomeration.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Beetle®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LuiCwr_Beetle-PPC130M-9249.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Mirel™ P4001	Metabolix	PHA	Mirel™
Retpol® 7157 TF HS	PolyPacific Pty. Ltd.	PP Copolymer	Retpol®
Gallonprene® GP540-8005	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Jianqiao PC/ABS	Shanghai Jianqiao Plastic Co., Ltd.	PC+ABS	Jianqiao
Hifax BC 72G C13055	LyondellBasell Industries	PP Copolymer	Hifax