InnoPlus LD2420F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LuRRcb_InnoPlus-LD2420F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Special Characteristics : InnoPlus LD2420F is produced by high pressure tubular process, a technology licensed by LyondellBasell. This grade offers excellent processability for increased extruder outputs, good balance of mechanical and optical properties, exceptional clarity and gloss. Typical Applications : InnoPlus LD2420F is recommended for producing the heavy duty films, liners, shrink hoods, bags & pouches and agricultural films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 260 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 11.0 | MPa | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 19.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 300 | % | |
| TD : Break, 50 µm, Blown Film | 600 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 110 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Melting Temperature | 111 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm, Blown Film) | > 40 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP514-434 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sylvin 9727-77 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Hydrin® T3100 | Zeon Chemicals L.P. | Epoxy | Hydrin® |
| Karina BLACK PVC COMPOUND -E 753D48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ EX03319C compound | SABIC Innovative Plastics Asia Pacific | PEI | LNP™ STAT-KON™ |