SECCO HIPS-622
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Shanghai SECCO Petrochemical Co., Ltd |
| Trademark: | SECCO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LtnRMY_SECCOHIPS622.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HIPS622 retains good fluidity, mould release and excellent rigidity. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.5 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.40 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 28.0 | MPa | ISO 527-2/50 |
| Fracture | 25.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 45 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress 2 | 48.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 73.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 3 | 92.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | in Oil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8693-65 Clear 8355 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| UMG WOOD® W300E | UMG ABS, Ltd. | ABS | UMG WOOD® |
| Amodel® A-1933 HSL | Solvay Specialty Polymers | PPA | Amodel® |
| Keyflex® BT 3038D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| LNP™ THERMOCOMP™ QC008 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |